Scholzite Diffraction data computed using the structure from the paper listed below, along with the cell parameters refined from the powder pattern for R050238 Taxer K J Zeitschrift fur Kristallographie 198 (1992) 239-253 Order-disorder and polymorphism of the compound with the composition of scholzite, CaZn2[PO4]2*2H2O Note: hypothetical idealized structure Note: x(O2) corrected CELL PARAMETERS: 17.14900 7.412000 6.667000 90.00000 90.00000 90.00000 SPACE GROUP: Pbcn X-RAY WAVELENGTH: 1.541838 2-THETA INTENSITY D-SPACING H K L 10.35 100.00 8.5872 2 0 0 13.05 6.56 6.8077 1 1 0 18.65 3.92 4.7672 1 1 1 19.63 20.27 4.5314 3 1 0 20.71 32.19 4.2965 2 1 1 20.72 16.96 4.2936 4 0 0 23.76 25.77 3.7497 3 1 1 24.04 8.58 3.7076 0 2 0 26.21 31.36 3.4039 2 2 0 26.73 2.45 3.3389 0 0 2 27.24 4.15 3.2776 1 0 2 27.50 19.80 3.2469 4 1 1 28.04 12.43 3.1853 1 2 1 28.67 4.78 3.1167 5 1 0 28.72 8.30 3.1120 2 0 2 29.48 3.37 3.0326 2 2 1 31.03 19.16 2.8842 3 0 2 31.20 11.02 2.8695 2 1 2 31.71 1.96 2.8243 5 1 1 31.75 4.15 2.8207 3 2 1 31.92 57.26 2.8062 4 2 0 33.36 25.07 2.6880 3 1 2 34.04 11.00 2.6357 4 0 2 34.70 2.84 2.5870 4 2 1 36.19 10.20 2.4835 4 1 2 36.23 5.07 2.4811 0 2 2 36.25 6.45 2.4795 6 1 1 36.62 10.63 2.4556 1 2 2 37.76 10.88 2.3836 2 2 2 38.20 2.56 2.3575 5 2 1 38.68 8.99 2.3293 7 1 0 39.24 1.33 2.2972 1 3 1 39.57 2.40 2.2784 5 1 2 39.61 8.82 2.2765 3 2 2 39.74 2.26 2.2692 3 3 0 39.80 25.38 2.2657 6 2 0 42.08 5.08 2.1482 4 2 2 42.11 1.87 2.1468 8 0 0 42.13 2.22 2.1456 6 2 1 43.41 5.30 2.0854 6 1 2 45.09 2.26 2.0113 5 2 2 45.21 5.83 2.0063 5 3 0 45.91 2.59 1.9771 7 0 2 46.00 1.70 1.9735 1 3 2 46.08 1.36 1.9703 8 1 1 46.43 1.03 1.9563 7 2 1 47.61 9.25 1.9104 7 1 2 47.66 11.32 1.9084 0 2 3 48.52 2.61 1.8768 3 3 2 48.57 1.15 1.8748 6 2 2 48.90 1.29 1.8630 2 2 3 49.16 1.82 1.8538 0 4 0 49.32 2.49 1.8480 9 1 0 50.37 13.45 1.8121 2 4 0 50.55 3.75 1.8058 8 0 2 51.03 1.52 1.7899 8 2 1 52.14 4.88 1.7545 8 1 2 53.27 4.64 1.7197 5 3 2 53.35 3.29 1.7174 10 0 0 53.87 1.01 1.7019 4 4 0 54.46 1.26 1.6849 7 3 1 55.29 12.67 1.6616 1 0 4 56.38 9.84 1.6321 6 3 2 56.81 1.37 1.6208 0 4 2 56.95 2.06 1.6169 9 1 2 57.08 4.41 1.6136 1 4 2 57.50 1.18 1.6027 3 0 4 57.90 5.16 1.5926 2 4 2 58.09 1.37 1.5879 6 2 3 58.22 1.15 1.5848 5 4 1 58.61 1.11 1.5751 8 3 1 59.25 1.75 1.5595 3 4 2 59.40 2.44 1.5560 6 4 0 59.91 7.62 1.5439 7 3 2 60.61 3.72 1.5278 11 1 0 60.63 1.11 1.5272 10 0 2 61.06 1.47 1.5176 10 2 1 61.11 5.36 1.5163 1 2 4 61.38 5.51 1.5105 9 3 0 61.78 2.50 1.5015 5 0 4 62.04 3.23 1.4958 10 1 2 63.20 6.42 1.4711 3 2 4 63.46 1.79 1.4658 5 4 2 63.83 5.51 1.4581 8 3 2 65.99 2.76 1.4156 6 1 4 66.26 2.15 1.4104 6 4 2 67.27 6.68 1.3917 5 2 4 67.40 4.89 1.3893 11 1 2 68.13 3.82 1.3762 9 3 2 68.96 1.44 1.3615 5 5 0 69.52 1.62 1.3520 4 4 3 69.57 1.21 1.3512 1 5 2 70.30 1.55 1.3388 2 5 2 71.52 1.09 1.3189 3 5 2 71.66 4.04 1.3168 4 3 4 72.78 1.77 1.2992 10 3 2 72.89 2.37 1.2975 8 1 4 73.04 3.54 1.2952 12 1 2 73.15 1.76 1.2935 7 2 4 73.22 1.42 1.2925 4 5 2 73.98 2.67 1.2811 3 1 5 74.37 1.59 1.2753 6 4 3 75.37 1.25 1.2608 5 5 2 77.06 2.79 1.2373 1 4 4 77.17 1.62 1.2359 0 6 0 77.85 1.32 1.2267 14 0 0 78.11 1.12 1.2233 2 6 0 78.94 2.99 1.2124 3 4 4 78.98 1.97 1.2119 13 1 2 81.41 2.11 1.1818 10 1 4 82.32 1.63 1.1710 9 5 0 82.82 1.90 1.1651 13 3 0 84.28 1.17 1.1486 2 6 2 85.27 1.52 1.1378 14 1 2 85.44 1.34 1.1360 3 6 2 85.86 1.06 1.1315 15 1 0 87.06 1.03 1.1190 4 6 2 87.06 1.03 1.1190 4 6 2 XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.