Barioferrite Collomb A, Wolfers P, Obradors X Journal of Magnetism and Magnetic Materials 62 (1986) 57-67 Neutron diffraction studies of some hexagonal ferrites: BaFe12O19, BaMg2-W and CaCo2-W Note: T = 470 C, neutron, refined with Rietveld Locality: synthetic _database_code_amcsd 0013058 CELL PARAMETERS: 5.9291 5.9281 23.4070 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 712.493 Density (g/cm3): 5.180 MAX. ABS. INTENSITY / VOLUME**2: 42.00431995 RIR: 2.640 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.68 4.03 5.0155 1 0 1 12 17.69 2.02 5.0147 0 1 1 12 18.87 7.56 4.7021 1 0 2 12 18.88 3.78 4.7014 0 1 2 12 22.79 10.10 3.9012 0 0 6 2 23.04 2.99 3.8596 1 0 4 12 28.74 1.21 3.1063 1 0 6 12 30.15 46.18 2.9646 1 1 0 6 30.55 14.96 2.9259 0 0 8 2 31.12 9.26 2.8738 1 1 2 12 31.94 89.73 2.8021 1 0 7 12 33.90 100.00 2.6445 1 1 4 12 34.95 9.38 2.5672 2 0 0 6 35.16 5.94 2.5521 2 0 1 12 35.31 7.45 2.5421 1 0 8 12 35.81 1.21 2.5077 2 0 2 12 36.86 45.91 2.4387 2 0 3 12 38.13 2.90 2.3604 1 1 6 12 38.81 2.04 2.3201 1 0 9 12 40.05 27.32 2.2511 2 0 5 12 42.13 17.11 2.1446 2 0 6 12 42.44 1.32 2.1298 1 0 10 12 46.18 5.83 1.9658 1 0 11 12 49.62 2.41 1.8371 1 1 10 12 49.91 7.87 1.8271 2 0 9 12 52.93 3.08 1.7297 2 0 10 12 53.55 7.88 1.7114 3 0 0 6 54.16 1.97 1.6936 3 0 2 12 54.68 35.84 1.6785 2 1 7 24 54.92 5.65 1.6719 0 0 14 2 55.98 19.65 1.6428 3 0 4 12 56.14 40.62 1.6383 2 0 11 12 56.47 3.05 1.6295 1 1 12 12 56.94 4.86 1.6173 2 1 8 24 59.42 1.35 1.5554 2 1 9 24 59.52 2.27 1.5532 2 0 12 12 62.17 1.49 1.4930 1 0 15 12 62.68 40.42 1.4823 2 2 0 6 63.06 2.50 1.4741 2 0 13 12 65.04 3.89 1.4339 2 1 11 24 66.77 10.63 1.4010 2 0 14 12 67.61 2.05 1.3856 2 2 6 12 71.33 5.30 1.3223 2 2 8 12 71.98 2.46 1.3119 1 1 16 12 72.08 12.40 1.3103 3 1 7 24 73.63 1.22 1.2865 3 0 12 12 74.03 1.16 1.2805 3 1 8 24 74.98 4.07 1.2667 4 0 3 12 75.40 2.57 1.2606 1 0 18 12 77.03 2.26 1.2380 4 0 5 12 78.43 1.35 1.2194 4 0 6 12 78.68 1.28 1.2161 2 1 15 24 78.89 1.33 1.2134 2 0 17 12 80.69 5.07 1.1909 1 1 18 12 81.29 1.94 1.1835 3 1 11 24 82.40 1.34 1.1703 0 0 20 2 84.09 1.24 1.1511 4 0 9 12 86.96 1.12 1.1203 4 1 0 12 87.77 1.33 1.1121 3 0 16 12 87.88 2.05 1.1110 3 2 7 24 88.06 6.59 1.1091 2 2 14 12 88.94 2.74 1.1005 4 1 4 24 89.07 7.69 1.0992 4 0 11 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.